Influence of pH value on the properties of the composite wires by chemical deposition
-
摘要: 采用电流化学镀工艺,在直径为100 m的铜丝上通以150 mA的直流电流,制备了NiCoP/CuBe复合结构丝,研究了镀液pH值对复合结构丝镀层的形貌、镀速、成分、磁性能和GMI效应的影响.研究发现,镀液pH值的改变会引起致密性、镀速、镀层成分和磁性能的变化,结果影响到材料的磁阻抗比和特征频率.pH值为8.4时,得到最大阻抗比为868%.Abstract: Composite wires of 100 m diameter CuBe coated with a layer of NiCoP were prepared by chemical plating, and dc current of 150 mA got through CuBe wires during the process. The influence of pH value on the composite wires was studied in terms of morphology, deposition speed, composition, magnetic property and the GMI effect. The results showed that the pH value influenced GMI effect and critical frequency by changing the roughness of materials, deposition speed, the coating composition and magnetic structure. The maximum GMI effect of 868% is obtained at the pH value of 8.4.
-
Key words:
- pH value /
- composite wire /
- chemical plating /
- GMI effect
-
[1] [1] LI B, SALEM N P M, GIOUROUDI I, et al. Integration of thin film giant magnetoimpedance sensor and surface acoustic wave transponder[J]. Journal of Applied Physics, 2012, 111(7): 7E-514E.[2] 郝建华,郑全普,胡然,等. 基于GMI效应的磁传感器研究与发展现状[J]. 国外电子测量技术,2011(4): 20-26.[3] ANTONOV A S, RAKHMANOV A L, BUZNIKOV N A, et al. Magnetic properties and magneto-impedance of cold-drawn permalloy-copper composite wires[J]. IEEE Trans Magn, 1999, 35(5): 3640-3642.[4] XIAO S, LIU Y, DAI Y, et al. Giant magnetoimpedance effect in sandwiched films[J]. Journal of applied physics, 1999, 85(8): 4127-4130.[5] YU R H, LANDRY G, LI Y F, et al. Magneto-impedance effect in soft magnetic tubes[J]. Journal of Applied Physics, 2000, 87(9): 4807-4809.[6] WANG X, YUAN W, ZHAO Z, et al. Giant magnetoimpedance effect in CuBe/NiFeB and CuBe/Insulator/NiFeB electroless-deposited composite wires[J]. IEEE Trans Magn, 2005, 41(1): 113-115.[7] ATALAY F E, KAYA H, ATALAY S. Effect of pH on the magnetoimpedance properties of electrodeposited CoNiFe microtubes[J]. Physica B, 2006, 371(2): 327-331.[8] 张庚华,程金科,王清江,等. pH 值对化学镀 CoNiP 复合丝 GMI 效应的影响[J]. 应用化学, 2008, 25(11): 1277-1280.[9] ATALAY F E, KAYA H, ATALAY S. Giant magnetoimpedance effect in electroplated CoNiFe/Cu wires with varying Ni, Fe and Co content[J]. Journal of Alloys and Compounds, 2006, 420(1-2): 9-14.[10] LUAN H Y, LI X, PAN H L, et al. Magnetic properties of composite wires prepared by chemical plating under DC current[J].Journal of Magnetism and Magnetic Materials, submitted.[11] 付宏波. 提高巨磁阻抗 (GMI) 效应的方法讨论[J]. 中国电子商务, 2011(1): 372-373.[12] PHAN M, PENG H. Giant magnetoimpedance materials: Fundamentals and applications[J]. Progress in Materials Science, 2008, 53(2): 323-420.[13] 刘珍. 溶液 pH 值对化学镀 Ni-Co-P 合金的影响[J]. 电镀与精饰, 1999, 21(1): 17.[14] 李宁. 化学镀实用技术[M]. 北京:化学工业出版社, 2004.
点击查看大图
计量
- 文章访问数: 1448
- HTML全文浏览量: 58
- PDF下载量: 1659
- 被引次数: 0