Influence of vacuum annealing on the GMI effect of Co81.5Fe4.5Mo2B12 microwires
-
摘要: 采用高频感应加热熔融快淬法制备了Co81.5Fe4.5Mo2B12玻璃包裹丝,研究了真空条件下退火对细丝巨磁阻抗效应及非对称性的影响.结果显示,随着退火温度的升高,玻璃包裹丝的巨磁阻抗效应先增大后减小.退火温度为250 ℃时,巨磁阻抗效应最明显;退火后样品的磁阻抗曲线对称性大都有所改善;退火温度为330 ℃时,磁阻抗曲线对称性遭到破坏,可能是磁各向异性降低所引起的.Abstract: Co81.5Fe4.5Mo2B12 microwires were prepared by the TaylorUlitovsky method. Influence of the vacuum annealing conditions on Giant Magnetoimpedance (GMI) effect and its symmetrical properties were studied. The results show that the GMI ratio increases firstly and then decreases with the increase of the annealing temperature. The highest GMI ratio was obtained when the temperature is 250 ℃. The symmetry of the GMI curves of the microwires may be improved after proper annealing. When the annealing temperature is 330 ℃, GMI symmetry of the microwire was deteriorated may be caused by the decrease of the magnetic anisotropy.
-
Key words:
- GMI (Giant magnetoimpedance) /
- microwires /
- hysteresis /
- vacuum annealing
点击查看大图
计量
- 文章访问数: 1021
- HTML全文浏览量: 38
- PDF下载量: 1147
- 被引次数: 0